Institute for Color Science and Technology (ICST) Progress in Color, Colorants and Coatings 2008-2134 15 2 2022 05 01 Experimental and Theoretical Investigation on the Corrosion Inhibitor Potential of N-MEH for Mild Steel in HCl 111 122 81763 10.30509/pccc.2021.166815.1111 EN A. K. Khudhair Ministry of Higher Education and Scientific Research, University of Technology, P.O. Box: 10001, Baghdad, Iraq A. M. Mustafa Production Engineering and Metallurgy, University of Technology, P.O. Box: 10001, Baghdad, Iraq M. M. Hanoon Production Engineering and Metallurgy, University of Technology, P.O. Box: 10001, Baghdad, Iraq A. Al-Amiery Production Engineering and Metallurgy, University of Technology, P.O. Box: 10001, Baghdad, Iraq Department of Chemical and Process Engineering, Faculty of Engineering & Built Environment, University Kebangsaan Malaysia, Bangi, Selangor 43600, Malaysia L. M. Shaker Department of Chemical and Process Engineering, Faculty of Engineering & Built Environment, University Kebangsaan Malaysia, Bangi, Selangor 43600, Malaysia T. Gazz Technical College Al-Musaib, Al-Furat Al-Awsat Technical University, P.O. Box: 51006, Babil, Iraq A. B. Mohamad Department of Chemical and Process Engineering, Faculty of Engineering & Built Environment, University Kebangsaan Malaysia, Bangi, Selangor 43600, Malaysia A. H. Kadhum College of Dentistry, Al-Ameed University, P.O. Box: 1238, Karbalaa, Iraq M. S. Takriff Department of Chemical and Process Engineering, Faculty of Engineering & Built Environment, University Kebangsaan Malaysia, Bangi, Selangor 43600, Malaysia Journal Article 2021 02 24 <em>There are significant losses at high costs for long periods due to the corrosion and damage it causes in most industrial processes, especially the oil and gas industries. The corrosion inhibition ability of N-methyl-2-(1-(5-methyl thiophene-2-yl) ethylidene) hydrazine carbothioamide (N-MEH) was examined. It was tested on mild steel in a 1 M hydrochloric acid solution. Gravimetric measurements and scanning electron microscopy (SEM) were used to confirm the effort compound as a corrosion inhibitor. The experimental results showed that the maximum inhibition efficacy of 95.3 % was performed at an optimal inhibitory concentration of 0.005 M and 303 K using weight loss techniques. SEM indicates that N-MEH molecules are absorbed onto the surface of mild steel. As a complementary technique, density functional theory (DFT) was used to look at the interactions between N-MEH molecules and mild steel surfaces. N-MEH molecules' adsorption on the surface of mild steel follows the processes of chemical and physical absorptions and obeys the Langmuir isothermal adsorption model.</em> https://pccc.icrc.ac.ir/article_81763_cf5e3fce22ef4134f1f3b75b5d65a7fe.pdf